Intoduction
Injection molding is one of the most common manufacturing methods to produce thin-wall engineered parts. Development of molds that produce high quality parts is a talent that develops with experience. Due to the time and effort required to develop a good set of tooling, it is not unusual for manufacturers to seek out injection molding machines that will be compatible with their molds, rather than trying to redesign molds to work on specific machines.
Design checklist
As designers of injection molded products you are probably well aware of design best practice. What you may not appreciate is the important contribution a well designed mould tool can make to the new product development process. The wrong decisions taken at the critical early stage of a project will add cost and time to mould tool design, manufacture and maintenance, put pressure on product launch dates, and, of course, adversely affect product manufacture and in-use performance.
1) Have you specified a material and grade before the mould tool is designed?
YES. Well done! Go to wall thickness.
NO. You are in trouble already!
2) Walls cool at different rates depending on thickness; have you taken this into account when designing your part, particularly at the junctions between thick and thin sections?
YES. Congratulations! Go to draft angles.
NO. Your part will suffer from sink and warpage unless you have designed-in ribs.
3) Have you added one degree draft on all non-textured walls, ribs, bosses and any other feature created in the line of tool opening?
YES. Good job! Follow the link to the next question about draft angles.
NO. The tool will need special parts, adding cost.
3) Have you added at least three degrees to all shut out faces (places where tool surfaces touch), for example, part openings?
YES. Keep up the good work! Go to the final question about draft angles.
NO. Tool wear will increase significantly, driving up maintenance costs and reducing tool life.
4) If your part is textured, have you increased draft angles accordingly?
YES. Give yourself a pat on the back! Go to ribs.
NO. It will be difficult to remove the part from the mould
5) Are the ribs that you have specified for strength - to avoid warpage and/or to add functionality - no more than 50% of the thickness of the walls with which they mate?
YES. How good is that! One more question on ribs.
NO. Your part will suffer from sink and warpage.
6) Are the ribs you have designed very thin or deep?
NO. Smashing! Go to bosses.
YES. This will add time and cost to tool production.
7) If you need bosses for screw fixings, have you specified a one degree draft angle and is the section no more than 50% of the thickness of the wall with which it mates?
YES. Way to go! Go to clips.
NO. The tool will need special parts, adding cost, and your part will suffer from sink.
8) If internal undercuts are required for fixing and location features, or because part geometry is the same in both sides of the mould tool, have you confirmed that the cores will move away from the undercut as the part is ejected?
YES. Magic! Go to external undercuts.
NO. The tool will not operate.
9) To produce the external undercuts required for holes and openings, or dictated by geometry of the total part, have you confirmed that the cores will operate as the tool opens?
YES. Cool! Go to split/parting lines.
NO. The part will get trapped.
10) Have you considered where the tool should be split so that it:
1. Follows a smooth path?
2. Can vent gases created during molding?
3. Avoids cosmetic and functional faces?
YES. Have three pats on the back! Go to part ejection.
NO. 1. Tool life will be reduced significantly and additional, less efficient cutting operations will add time and cost
2. You risk burning the part and trapping gas
3. Appearance will be compromised and functional faces will have witness lines
11) The selection of an ejector type depends on part geometry and features such as bosses; have you considered how your part will be ejected from the mould?
YES. Brilliant! Go to feeding.
NO. Insufficient ejection risks the part distorting or suffering from stress marking.
To ensure optimum filling, have you specified the location and type of feed gate before the mould tool is designed?
YES. One more to go! Go to cooling.
NO. Parts of the mould will not be sufficiently filled, causing sink and warpage.
12) To ensure optimum processing of the material, mould temperature must be correctly controlled; have you considered how the mould can be heated and cooled?
YES. You’ve done it!
NO. 1. The mould will not fill correctly
2. Material properties will be affected
3. Part dimensions will not be correct
4. The part will be distorted
Sink marks...
...are caused when a wall section is either too thick or there is a sudden change in section, typically where ribs and bosses are placed internally or where the extremity of the part is the same section or larger than the area where the feed is occurring. Cosmetic appearance is affected and dimensional accuracy will be lost. In extreme cases there will be a void inside the part potentially leading to mechanical failure. Some materials are more susceptible to sink than others with polypropylene and polyamide the worst culprits.
Warpage...
...like sink is caused when the section is either too thick or there is a sudden change in section and there is insufficient strength in the part to hold the required shape. Appearance and dimensional accuracy are affected. All materials will warp but polypropylene and polyamide perform particularly badly.
Fig.1 Complete Mold Assembly & mold manufacturing workflow
Ribs
Gussets
Bosses
Radii, Fillets and Corners
Mold Heating
A uniform mold temperature means that the temperature of each half of the mold is the same (within ±3°C (5°F)) for all locations when the mold is heated by oil or steam. Molds that are heated with electric cartridge heaters can vary by as much as 6°C (10°F). A mold with a uniform temperature will fill easier and produce parts with less warpage, improved dimensional stability and a uniform surface appearance. Achieving a uniform mold temperature is dependent on your method of mold heating. A mold that is heated by steam or oil will have a uniform mold temperature because the heat source maintains a constant temperature. However, oil, as a heat source, is only about half as efficient as steam. Therefore, when using oil to heat a mold, it is necessary to set the oil temperature higher than the desired mold temperature. Electrically heated molds are more difficult to maintain at a uniform temperature because the cartridge heaters are constantly cycling on and off. When they are on, they generate a great deal of heat at the source, but this heat must be distributed throughout the mold in a way that produces a uniform mold temperature.
To determine the amount of wattage needed to heat a mold, the use of the following formula might be helpful: 1¼ kilowatts for every 45 kg (100 pounds) of mold steel. Note: This formula normally will allow the mold to be heated to molding temperatures in 1 to 2 hours. Locating a heater on the centerline of the mold is not recommended, because the center of the mold is normally hot enough without adding any additional heat. Typically, the cartridge heaters are located in the support plates with a distance of 64 mm (2 ½") between heaters.
NOTE: Deep draw molds may need to also have heaters in the retainer plate. There should be a minimum of one thermocouple to control each half of the mold. In larger molds, it is recommended to have more than one thermocouple in each mold half. This will result in better control and more uniform mold temperatures. The thermocouples should be located in the “A” and “B” plates, between two heaters if possible and at a distance of 32 mm - 38 mm (1¼" - 1½") from the closest cartridge heater. This distance is to be measured from the edge of thermocouple hole to the edge of the cartridge heater hole. The distance from the thermocouple to the heater is important because a heater that is too close will cause the thermocouple to turn off the heat before the mold is at temperature. A heater that is too far away from the thermocouple will result in a mold that overheats and then gets too cool. Likewise, it is not a good practice to position a thermocouple so it senses the external surface temperature of the mold. If possible, it should be located 38 mm - 51 mm (1½" - 2") inside the mold, since the temperature taken there, is less susceptible to outside influences and therefore more stable.
When injection molding with multiple cavity molds, it is important that all the cavities are filled simultaneously. The most common means to achieve a balanced fill is to make the distance the material travels from the sprue to each cavity the same. This approach will work as long as the material flows directly from the sprue to the gate of the part. However, if the runner is divided two or three times in going from the sprue to the gate, it is unlikely that the fill will be balanced. An effective way of balancing the fill is to have one main runner that extends from the last cavity on one end of the mold to the last cavity on the opposite end, with sub-runners feeding the individual cavities. To balance the fill of the cavities, flow resistor pins are placed in the sub runners. These pins are adjusted to inhibit the flow of material to the individual cavities so all the cavities are filled at the same time.
Venting
When molding thermosets, the polymerization process that takes place produces volatiles, which along with the air already within the cavity chamber, can become trapped and superheat to 375°C - 425°C (700°F - 800°F). If the gases are not allowed to escape through vents, they may oxidize the lubricants leaving burn marks on the part. The vents allow the volatiles to escape to atmosphere.
In addition to visual problems, improper venting will result in parts that cannot be filled, have dimensional problems or have less than the expected physical and/or electrical strengths. The first question that has to be addressed is vent location. It is important that all vents must lead to the atmosphere otherwise the vent will be useless. Unless the part geometry shows some obvious locations for vents, a brief molding trial should be conducted to observe where the gas voids occur.
Whenever possible, vents should be located in the movable half of the mold, wherever a gas void or knit line is seen on a part. Vents for phenolic parts should be 6 mm (¼") wide and 0.08 mm - 0.09 mm (0.003" - 0.0035") deep and vents for polyester parts should be 6 mm (¼") wide and 0.05 mm - 0.06 mm (0.002" - 0.0025") deep. The width is not as critical as the depth. A vent that is 0.025 mm (0.001") or less, is too shallow and may seal when the mold is closed. A vent that is 0.13 mm (0.005") is normally too deep and may not seal. As a result, internal cavity pressure will be low and the shrinkage, the physical and the electrical properties may not match data sheet values. Of equal importance to the location and depth of the vents is vent length, which is the distance from the part that the vent maintains its 0.08 mm (0.003") depth. The vent should be approximately 25 mm (1") long to allow pressure to build in the cavity after the material in the vent cures. After this point, the vent can be relieved to a depth of 0.25 mm - 0.50 mm (0.01" - 0.02"). To help the vent stay with the part, the corner of the vent at the part edge can be radiuses or chamfered. It is sometimes necessary to vent “dead” areas of the mold with vented ejector pins. Before adding the vents, an ejector pin should fit the hole in which it will operate within 0.025 mm (0.001"). A flat is then ground on the diameter no deeper than 0.13 mm (0.005") for a distance that will take the vent 3 mm (_") below the fit length of the pin. Normally, the fit length should be 13 mm - 16 mm (½" - _") . (See sketch below) In addition, the stroke of the ejectors should be long enough for the entire vent plus 3 mm (_") to come up above the bottom of the cavity. This is so the vent can be self-cleaning or so an operator can blow the flash off the pins.
Something that is often overlooked in venting is the polish. It is recommended that all vents be draw polished in the direction of flow to at least the same finish as the cavities and cores. They should be polished for their entire length including the relieved distance. If a mold is to be chrome plated, all the molding surfaces should be polished and plated including the vents.
Sprues
The orifice of the sprue bushing must always be larger than the I.D. of the nozzle of the press. Normally, the sprue bushing should have an orifice that is 0.8 mm (1/32") larger than the press nozzle orifice. This difference in diameters helps the sprue pull out of the nozzle and the stationary half of the mold. The spherical radius of the nozzle should match the spherical radius of the sprue bushing. Alignment of the nozzle and sprue bushing can be checked by, pinching a piece of paper between them. Care should obviously be taken to not injure ones self or anyone else when conducting this check. In addition to checking the alignment, this same check will tell if the nozzle and sprue bushing are fitting together tightly or if they are damaged and causing leakage. We suggest that the new molds start out with a sprue bushing orifice of 6 mm (7/32") Dia. with a corresponding nozzle orifice of 5 mm (3/16") Dia. These diameters are considered fairly small for thermoset materials and forcing the material through these diameters, should produce frictional heat in the material that can help to reduce the overall cycle times. Many times the largest cross section in the mold is found at the base of the sprue bushing. By changing from a typical 7 mm (9/32") Dia. Sprue bushing orifice to the smaller 6 mm (7/32") Dia. Orifice the diameter at the base of the sprue bushing will also be reduced 1.5 mm (1/16"). A small change like this can sometimes result in a cycle time reduction. Sometimes, for no apparent reason, you will have a significant number of nozzle freeze ups. A possible cause is too much heat being transferred from the mold to the nozzle. With a 165°C (330°F) mold and a 110°C (230°F) nozzle, the natural tendency will be for the mold to heat the nozzle. One way to reduce the heat transfer is to use a nozzle with a 12.7 mm (½") spherical radius nozzle with a sprue bushing that has a 19 mm (¾") spherical radius. This reduces the surface area of contact between the nozzle and the mold. Water cooled sprues can be used to eliminate the scrap, if you are molding polyester. However, if molding phenolic or melamine-phenolic parts, using water cooled sprue may result in frequent nozzle freeze ups. Sprue bushings typically are only hardened to 43-45 HRC. The runners, cores and cavities of a typical mold for thermoset materials are hardened to a minimum of 52-54 HRC. Because the sprue bushings are relatively soft, they wear out fairly quickly and a worn sprue bushing can cause sprues to stick in the stationary mold half. To improve the wear resistance of sprue bushings used in molds for thermoset materials, we suggest using sprue bushings made out of D-2 steel. These sprue bushings can be hardened to 62 HRC and they will also have higher chrome content than conventional sprue bushings. Both of these qualities should improve the wear resistance and the release properties of the sprue bushing.
Sprue Pullers
In order to insure that the sprue comes out of the sprue bushing and stays with the runner, a sprue puller is used. As can be seen in the sketch, a 5° reverse taper on the puller that starts at the runner and extend 8 mm (5/16") below the runner is recommended. In addition, a small radius (approximately 1.5 mm (1/16")) at the junction of the puller and the runner and a larger radius (approximately 6 mm (¼")) at the junction of the sprue and the runner is used to help hold the sprue, runner and sprue puller together. The added step on the bottom of the sprue puller is an aid to the removal of the sprue and sprue puller.
Sprue Bushing Locator Ring
Standard locating rings provide no support for the center of the mold. In some cases it may be necessary to have support in the middle of the stationary side of the mold. (i.e. heavy flashing in the center of the mold.) Stationary side support can be accomplished by switching to the modified locating ring shown below. This type design allows the center of the stationary side to be "domed", by placing shims under the locator ring.
Runner Design
When designing runners for molds, there are a number of possible approaches. These include the standard full round with a centerline.
This is the most efficient runner, but in some cases it is necessary for the runner to be in only one half of the mold. A standard trapezoid runner is often used in situations that require the runner to be only in one mold half. The effective runner size is shown in the figure to the left. The four corners become "dead" areas with nearly no material movement. To reduce the amount of scrap in the runner, a modified trapezoid runner design is suggested. This design reduces the dead areas without a significant change to the effectiveness of the runner.
Gates
The gates for thermoset molds are high wear areas of the mold and therefore, need to be designed with this thought in mind. The gate should be made using a replaceable insert so when the gate becomes badly worn it can be easily replaced. A gate should be made of materials that do not wear easily. Three materials commonly used for gate inserts are carbide, D-2 steel and CPM-10V particle steel made by Crucible Steel. In addition to inserting the gate, it is beneficial to insert the mold opposite the gate and at the impingement area in the cavity. These areas are also high wear locations and will need some maintenance as the mold is run. When designing an edge gate for thermoset materials, the width of the gate can be as small as 1.5 mm (1/16") but the depth of the gate should not be less than 1.3 mm (0.050"). A gate should be large enough to allow the part to fill within the range of injection pressure and injection time that Plenco suggests in the material’s “Injection Molding Startup Procedure” section. Avoid using multiple gates on parts to minimize the number of knitlines. A knitline is created when two fronts of material meet. Knitlines are weaker than the rest of the part because there is not as much cross linking that takes place across the knit as there is in the main body of the part. To keep the overall strength of the parts as high as possible, the number of knitlines should be kept to a minimum. A second type of gate that is widely used in molds processing thermoset materials is the subgate. This type of gate is sometimes referred to as a tunnel gate. The advantage of a subgate is it shears off as the part is ejected from the mold. As a result, there is no need for a secondary operation to remove the gate nor is there any concern that the gate will project out from the part and become an assembly or a visual problem. In addition to the gate removal feature, the subgate can sometimes be designed to direct the flow of material towards a difficult to fill location. In this way, the part can be made easier to fill, which can have a positive effect on cycle times and scrap rates. Gate size is dependent on the size of the part. Typically 0.13mm (0.050") can be used for small parts and 0.20mm (0.080") for larger parts. There are some problems associated with using subgates, which include:
The tip of the gate breaking off and sticking in the mold. This is especially true for polyester molding materials and therefore, the use of subgates in molds for polyester parts is not recommended. The amount of steel at the parting line above the gate being too thin which results in the metal wearing away very quickly after the mold begins to produce parts.To reduce the likelihood of the gate tip breaking off and sticking in the mold, the tunnel needs to be well polished so all EDM pits are removed. Locating an ejector pin at least 38 mm (1½") from the tunnel allows the runner to flex and pull the gate out of the mold without breaking. It is also important to design the tunnel so the angle of incidence with the part allows the gate to pull, but keeps sufficient thickness of steel at the parting line to prevent breakage. See the sketch for further clarification.
Recent developments in thermoset injection molding have shown that a part can be molded with nearly all signs of the gate gone. This is done using a gate cutter. A gate cutter is a blade or a pin that is located in the mold directly below the gate. Immediately after the material is injected into the cavity, this blade is advanced forward to seal off the gate. Once the lade is in the forward position, the material cures against it, producing the same finish as the rest of the part. The only visible trace of a gate is a witness line.
Cavities and Core
In nearly all molds, the use of inserted cavities and cores is encouraged. The primary reason for this is in the event of an individual cavity or core being damage, that particular cavity can be removed from the mold and repaired while the rest of the mold is put back into service. Having individual cavities also allows for insert changes that make it possible to run multiple versions of the same basic part simultaneously. When the parts are very small and there are a large number of cavities, individual cavity inserts might not be feasible. In those situations, we would suggest using cavity inserts of 3 or 4 cavities. The materials most commonly used for cavity inserts are H-13 and S-7. Both of these materials will harden to Rockwell 52 to 54 HRC and can be polished to produce an excellent surface finish on the parts.
Ejector Pin Location and Design
Without ejector pins, it is usually not possible to remove the molded part from the mold. The placement of the ejector pins is almost as critical as the location of the gate. The pins should push the part out of the mold without distorting it and without leaving an objectionable mark on the part. A secondary reason for having ejector pins is to aid in the venting of the mold. Ejector pins should be located in the deepest points of the cavity or core. We specifically suggest that ejector pins be located on the deepest points of ribs and bosses. If ejector pins are not located correctly, the part has to be “pulled” out of the deeper areas or the mold. Parts that have to be “pulled” out of the mold are more likely to stick or be distorted during ejection. (See sketch below.)
Once the location of the ejector pins is determined, the pin size needs to be decided upon. Very small diameter ejector pins can be problematic because of their susceptibility to breaking. Therefore, ejector pins smaller in diameter than 2.4 mm (3/32") are not recommended. Another common problem is material flowing down around the ejector pin and jamming it so it breaks when the ejectors are actuated. To prevent this from happening, the hole for the pin should only be 0.025 mm (0.001") larger than the pin for a depth of 13 mm - 16 mm (½" - _") from the cavity. Making it deeper can result in the pin binding and breaking.
To ensure that the ejector plate moves along the centerline of the ejector pins, it is suggested that the mold be equipped with a guided ejector system. In addition to aligning the ejectors, the guided ejector system moves the load of the ejector plate and the retainer plate from the ejector pins to the guide pins and bushings of the ejector system. While aligning the ejector holes in the mold with those in the retainer plate is always important, with a guided ejector system the alignment is even more critical. While it is desirable to have the ejector pins located on flat surfaces, this is not always possible. It is sometimes necessary to locate ejector pins on contoured surfaces. Ejector pins located on contoured surfaces should be made to match the contour of the cavity. It will be necessary to key these pins so they will maintain their alignment with the contour of the cavity. Sometimes parts may want to stay in the stationary mold half or a mold designer will install a stationary side ejector system as a precaution. For a compression or transfer mold this is not a problem. However, adding an ejection system to the stationary half of an injection mold can be complicated, since it will add 76.2mm – 101.6mm (3” – 4”) to the height of the mold. Therefore the amount of press daylight will need to be reviewed to make sure the mold can be opened and the parts ejected. This added length will not only increase the amount of scrap, but due to the larger sprue diameter at the parting line, the cycle time may have to be increased.
Polishing and Plating
The trend has been to cut back on polishing because of its high cost. Molds are being made that still show cutter marks on the non-visible areas of the parts. While this practice may save money in the construction of the mold, it may increase part costs due to high scrap and down time. The non-polished areas will generate frictional heat in the material as it passes over these areas. This added heat can cause the material to cure prior to filling the part. These unpolished areas can change the filling pattern of the material, which can result in gas being trapped in locations that can not be vented. For these reasons, that it is suggested that all molding surfaces be polished to a minimum of SPI #2 rating. The mold surfaces to be polished include the cavities and cores, the vents, the gates, the runners, the sprue and the entire parting line. The reason for polishing the parting line is to insure that any flash that may occur on it will come off of the mold with a minimal amount of effort.
When polishing a mold, care should be taken to be sure to always polish in the direction of draw. Vents need to be polished in the direction of material flow and they should have the same degree of polish as the cavity and core. Flat surfaces that have no influence on the removal of the part can be polished in any direction. When polishing deep ribs that were cut using the EDM process, it is important to be sure to polish out all of the EDM pit marks. Otherwise, there may be a problem with the rib breaking off of the part and sticking in the mold. After the mold is completely polished, then it is ready to be plated. Please keep in mind that any defect in the steel surface will not be covered by the plating, but will be accentuated by it. While there are a number of different types of plating available, to date, chrome plated molds provide the best part release and with the best part finish. Because some materials have fillers that are incompatible with nickel, the use of nickel or electrolysis nickel to plate molding surfaces is discouraged. In addition, nickel plating lacks the wear resistance of chrome plating. The surfaces to be plated should include the cores, the cavities, the core pins, the ends of the ejector pins, the runner blocks, the vents, and the entire parting line. To protect the molding surfaces and to insure good part release, it is necessary to plate all the surfaces that were polished. After the mold is plated, it will be necessary to repolish the chrome because unpolished chrome plating may cause sticking.
Center Supports
Often we find that molds built to run thermoset materials have little or no support in the middle. This will result is heavy flash around the sprue and parts that vary in thickness from the sprue side to the side opposite. To resolve this problem we suggest installing substantial support pillars down the center of the mold between the parallels (50.8mm (2”) dia. If possible).
High Centering the Mold
Sometimes the center of a mold will have heavy flash even with good center support. In these cases it may be necessary to do what we call “Doming the Mold” or “High Centering the Mold”. This is accomplished by placing a 0.0508mm – 0.0762mm (0.002” or 0.003”) shim on the support pillars in the center of the mold, which will cause the moving side of the mold to be slightly domed. On the stationary side of the mold we suggest using the modified locating ring shown below, that can also be shimmed 0.0508mm – 0.0762mm (0.002” or 0.003”) so this side of the mold can also be domed.
Side Locks
Injection-Compression molds require non tapered side locks and are also necessary for any molds where maintaining the alignment of the mold halves is critical to meeting the quality requirements of the part. They should be located on all four sides of the mold. The overall design of Progressive Components’ side locks is very good, since they have a longer engagement and are thicker.
Injection-Compression Mold
We suggests the following items be used in designing an Injection/Compression mold. (Also see sketch below)
• The clearance between the cavity and core should be 0.0254mm – 0.0508mm (0.001’ - 0.002”) per side.
• The engagement of the cavity into the core should be 19.050mm (0.750”).
• The shutoff around each cavity should be 0.0254mm – 0.0508mm (0.001” - 0.002”).
• The “pancake” thickness should be 0.152mm – 0.203mm (0.006” - 0.008”).
• A vent should be ground into the plunger directly opposite the sprue. This vent should start out at a depth of 0.127mm (0.005”).
• There should be a mismatch in radii between the plunger and cavity as shown, so the ejector pins have material to push against.
• The ejector pins for the “pancake” should be located around the perimeter for better and more complete flash removal.
• To prevent damaging the parting line around each cavity, landing blocks should be added that have an area equal to the maximum clamp tonnage of the press divided by 5.
Because of the close fit of the plunger and cavity, we recommend the use of non-tapered side locks to align the core and cavity.
Types of injection moulding machines
The types of injection machinery available differ basically in the method of heating and preplasticisation of the compounded rubber. The main difference usually arises between vertically oriented machines, which include both ram and screw-ram presses, and horizontally oriented machines, which are of the reciprocating screw type. In the former the mold temperature is maintained by conduction from the heated platens of the press, whereas the heaters are integral with the mold in the latter case. The configuration of molds for horizontal machines often result in large surface areas for potential convective heat loss and long paths for conductive heat flow from the press platens. The horizontal machine generates its own preplasticising heat by work on the rubber, which is fed into it in strip form, between the screw and the barrel. This heat is governed by a temperature-controlled fluid medium (water, glycol, or oil), which circulates around the barrel and, in larger machines, through the center of the screw. Progression of the rubber up the screw both heats and preplasticises it. The rubber, collected in front of the screw, pushes the screw back until a trip switch is operated, and the preplasticisation phase is completed. Final heating of the stock takes place during passage through a small die into the runner system of the mold. The second type of injection press uses the principle of vertical injection. This type of machine has a separate screw and injection piston in a V-head configuration situated near a vertical upstroking press. The preplasticising screw feeds into the injection chamber through a non-return valve where the compound is injected into the mold. There are many independently adjustable parameters of both the injection head and press unit. Molds for vertically oriented machines are usually larger in plan area, giving improved conductive heating, and also expose smaller areas for convective heat loss.
Injection molding is one of the most common manufacturing methods to produce thin-wall engineered parts. Development of molds that produce high quality parts is a talent that develops with experience. Due to the time and effort required to develop a good set of tooling, it is not unusual for manufacturers to seek out injection molding machines that will be compatible with their molds, rather than trying to redesign molds to work on specific machines.
Design checklist
As designers of injection molded products you are probably well aware of design best practice. What you may not appreciate is the important contribution a well designed mould tool can make to the new product development process. The wrong decisions taken at the critical early stage of a project will add cost and time to mould tool design, manufacture and maintenance, put pressure on product launch dates, and, of course, adversely affect product manufacture and in-use performance.
1) Have you specified a material and grade before the mould tool is designed?
YES. Well done! Go to wall thickness.
NO. You are in trouble already!
2) Walls cool at different rates depending on thickness; have you taken this into account when designing your part, particularly at the junctions between thick and thin sections?
YES. Congratulations! Go to draft angles.
NO. Your part will suffer from sink and warpage unless you have designed-in ribs.
3) Have you added one degree draft on all non-textured walls, ribs, bosses and any other feature created in the line of tool opening?
YES. Good job! Follow the link to the next question about draft angles.
NO. The tool will need special parts, adding cost.
3) Have you added at least three degrees to all shut out faces (places where tool surfaces touch), for example, part openings?
YES. Keep up the good work! Go to the final question about draft angles.
NO. Tool wear will increase significantly, driving up maintenance costs and reducing tool life.
4) If your part is textured, have you increased draft angles accordingly?
YES. Give yourself a pat on the back! Go to ribs.
NO. It will be difficult to remove the part from the mould
5) Are the ribs that you have specified for strength - to avoid warpage and/or to add functionality - no more than 50% of the thickness of the walls with which they mate?
YES. How good is that! One more question on ribs.
NO. Your part will suffer from sink and warpage.
6) Are the ribs you have designed very thin or deep?
NO. Smashing! Go to bosses.
YES. This will add time and cost to tool production.
7) If you need bosses for screw fixings, have you specified a one degree draft angle and is the section no more than 50% of the thickness of the wall with which it mates?
YES. Way to go! Go to clips.
NO. The tool will need special parts, adding cost, and your part will suffer from sink.
8) If internal undercuts are required for fixing and location features, or because part geometry is the same in both sides of the mould tool, have you confirmed that the cores will move away from the undercut as the part is ejected?
YES. Magic! Go to external undercuts.
NO. The tool will not operate.
9) To produce the external undercuts required for holes and openings, or dictated by geometry of the total part, have you confirmed that the cores will operate as the tool opens?
YES. Cool! Go to split/parting lines.
NO. The part will get trapped.
10) Have you considered where the tool should be split so that it:
1. Follows a smooth path?
2. Can vent gases created during molding?
3. Avoids cosmetic and functional faces?
YES. Have three pats on the back! Go to part ejection.
NO. 1. Tool life will be reduced significantly and additional, less efficient cutting operations will add time and cost
2. You risk burning the part and trapping gas
3. Appearance will be compromised and functional faces will have witness lines
11) The selection of an ejector type depends on part geometry and features such as bosses; have you considered how your part will be ejected from the mould?
YES. Brilliant! Go to feeding.
NO. Insufficient ejection risks the part distorting or suffering from stress marking.
To ensure optimum filling, have you specified the location and type of feed gate before the mould tool is designed?
YES. One more to go! Go to cooling.
NO. Parts of the mould will not be sufficiently filled, causing sink and warpage.
12) To ensure optimum processing of the material, mould temperature must be correctly controlled; have you considered how the mould can be heated and cooled?
YES. You’ve done it!
NO. 1. The mould will not fill correctly
2. Material properties will be affected
3. Part dimensions will not be correct
4. The part will be distorted
Sink marks...
...are caused when a wall section is either too thick or there is a sudden change in section, typically where ribs and bosses are placed internally or where the extremity of the part is the same section or larger than the area where the feed is occurring. Cosmetic appearance is affected and dimensional accuracy will be lost. In extreme cases there will be a void inside the part potentially leading to mechanical failure. Some materials are more susceptible to sink than others with polypropylene and polyamide the worst culprits.
Warpage...
...like sink is caused when the section is either too thick or there is a sudden change in section and there is insufficient strength in the part to hold the required shape. Appearance and dimensional accuracy are affected. All materials will warp but polypropylene and polyamide perform particularly badly.
Fig.1 Complete Mold Assembly & mold manufacturing workflow
Ribs
Gussets
Bosses
Radii, Fillets and Corners
Mold Heating
A uniform mold temperature means that the temperature of each half of the mold is the same (within ±3°C (5°F)) for all locations when the mold is heated by oil or steam. Molds that are heated with electric cartridge heaters can vary by as much as 6°C (10°F). A mold with a uniform temperature will fill easier and produce parts with less warpage, improved dimensional stability and a uniform surface appearance. Achieving a uniform mold temperature is dependent on your method of mold heating. A mold that is heated by steam or oil will have a uniform mold temperature because the heat source maintains a constant temperature. However, oil, as a heat source, is only about half as efficient as steam. Therefore, when using oil to heat a mold, it is necessary to set the oil temperature higher than the desired mold temperature. Electrically heated molds are more difficult to maintain at a uniform temperature because the cartridge heaters are constantly cycling on and off. When they are on, they generate a great deal of heat at the source, but this heat must be distributed throughout the mold in a way that produces a uniform mold temperature.
To determine the amount of wattage needed to heat a mold, the use of the following formula might be helpful: 1¼ kilowatts for every 45 kg (100 pounds) of mold steel. Note: This formula normally will allow the mold to be heated to molding temperatures in 1 to 2 hours. Locating a heater on the centerline of the mold is not recommended, because the center of the mold is normally hot enough without adding any additional heat. Typically, the cartridge heaters are located in the support plates with a distance of 64 mm (2 ½") between heaters.
NOTE: Deep draw molds may need to also have heaters in the retainer plate. There should be a minimum of one thermocouple to control each half of the mold. In larger molds, it is recommended to have more than one thermocouple in each mold half. This will result in better control and more uniform mold temperatures. The thermocouples should be located in the “A” and “B” plates, between two heaters if possible and at a distance of 32 mm - 38 mm (1¼" - 1½") from the closest cartridge heater. This distance is to be measured from the edge of thermocouple hole to the edge of the cartridge heater hole. The distance from the thermocouple to the heater is important because a heater that is too close will cause the thermocouple to turn off the heat before the mold is at temperature. A heater that is too far away from the thermocouple will result in a mold that overheats and then gets too cool. Likewise, it is not a good practice to position a thermocouple so it senses the external surface temperature of the mold. If possible, it should be located 38 mm - 51 mm (1½" - 2") inside the mold, since the temperature taken there, is less susceptible to outside influences and therefore more stable.
When injection molding with multiple cavity molds, it is important that all the cavities are filled simultaneously. The most common means to achieve a balanced fill is to make the distance the material travels from the sprue to each cavity the same. This approach will work as long as the material flows directly from the sprue to the gate of the part. However, if the runner is divided two or three times in going from the sprue to the gate, it is unlikely that the fill will be balanced. An effective way of balancing the fill is to have one main runner that extends from the last cavity on one end of the mold to the last cavity on the opposite end, with sub-runners feeding the individual cavities. To balance the fill of the cavities, flow resistor pins are placed in the sub runners. These pins are adjusted to inhibit the flow of material to the individual cavities so all the cavities are filled at the same time.
Venting
When molding thermosets, the polymerization process that takes place produces volatiles, which along with the air already within the cavity chamber, can become trapped and superheat to 375°C - 425°C (700°F - 800°F). If the gases are not allowed to escape through vents, they may oxidize the lubricants leaving burn marks on the part. The vents allow the volatiles to escape to atmosphere.
In addition to visual problems, improper venting will result in parts that cannot be filled, have dimensional problems or have less than the expected physical and/or electrical strengths. The first question that has to be addressed is vent location. It is important that all vents must lead to the atmosphere otherwise the vent will be useless. Unless the part geometry shows some obvious locations for vents, a brief molding trial should be conducted to observe where the gas voids occur.
Whenever possible, vents should be located in the movable half of the mold, wherever a gas void or knit line is seen on a part. Vents for phenolic parts should be 6 mm (¼") wide and 0.08 mm - 0.09 mm (0.003" - 0.0035") deep and vents for polyester parts should be 6 mm (¼") wide and 0.05 mm - 0.06 mm (0.002" - 0.0025") deep. The width is not as critical as the depth. A vent that is 0.025 mm (0.001") or less, is too shallow and may seal when the mold is closed. A vent that is 0.13 mm (0.005") is normally too deep and may not seal. As a result, internal cavity pressure will be low and the shrinkage, the physical and the electrical properties may not match data sheet values. Of equal importance to the location and depth of the vents is vent length, which is the distance from the part that the vent maintains its 0.08 mm (0.003") depth. The vent should be approximately 25 mm (1") long to allow pressure to build in the cavity after the material in the vent cures. After this point, the vent can be relieved to a depth of 0.25 mm - 0.50 mm (0.01" - 0.02"). To help the vent stay with the part, the corner of the vent at the part edge can be radiuses or chamfered. It is sometimes necessary to vent “dead” areas of the mold with vented ejector pins. Before adding the vents, an ejector pin should fit the hole in which it will operate within 0.025 mm (0.001"). A flat is then ground on the diameter no deeper than 0.13 mm (0.005") for a distance that will take the vent 3 mm (_") below the fit length of the pin. Normally, the fit length should be 13 mm - 16 mm (½" - _") . (See sketch below) In addition, the stroke of the ejectors should be long enough for the entire vent plus 3 mm (_") to come up above the bottom of the cavity. This is so the vent can be self-cleaning or so an operator can blow the flash off the pins.
Something that is often overlooked in venting is the polish. It is recommended that all vents be draw polished in the direction of flow to at least the same finish as the cavities and cores. They should be polished for their entire length including the relieved distance. If a mold is to be chrome plated, all the molding surfaces should be polished and plated including the vents.
Sprues
The orifice of the sprue bushing must always be larger than the I.D. of the nozzle of the press. Normally, the sprue bushing should have an orifice that is 0.8 mm (1/32") larger than the press nozzle orifice. This difference in diameters helps the sprue pull out of the nozzle and the stationary half of the mold. The spherical radius of the nozzle should match the spherical radius of the sprue bushing. Alignment of the nozzle and sprue bushing can be checked by, pinching a piece of paper between them. Care should obviously be taken to not injure ones self or anyone else when conducting this check. In addition to checking the alignment, this same check will tell if the nozzle and sprue bushing are fitting together tightly or if they are damaged and causing leakage. We suggest that the new molds start out with a sprue bushing orifice of 6 mm (7/32") Dia. with a corresponding nozzle orifice of 5 mm (3/16") Dia. These diameters are considered fairly small for thermoset materials and forcing the material through these diameters, should produce frictional heat in the material that can help to reduce the overall cycle times. Many times the largest cross section in the mold is found at the base of the sprue bushing. By changing from a typical 7 mm (9/32") Dia. Sprue bushing orifice to the smaller 6 mm (7/32") Dia. Orifice the diameter at the base of the sprue bushing will also be reduced 1.5 mm (1/16"). A small change like this can sometimes result in a cycle time reduction. Sometimes, for no apparent reason, you will have a significant number of nozzle freeze ups. A possible cause is too much heat being transferred from the mold to the nozzle. With a 165°C (330°F) mold and a 110°C (230°F) nozzle, the natural tendency will be for the mold to heat the nozzle. One way to reduce the heat transfer is to use a nozzle with a 12.7 mm (½") spherical radius nozzle with a sprue bushing that has a 19 mm (¾") spherical radius. This reduces the surface area of contact between the nozzle and the mold. Water cooled sprues can be used to eliminate the scrap, if you are molding polyester. However, if molding phenolic or melamine-phenolic parts, using water cooled sprue may result in frequent nozzle freeze ups. Sprue bushings typically are only hardened to 43-45 HRC. The runners, cores and cavities of a typical mold for thermoset materials are hardened to a minimum of 52-54 HRC. Because the sprue bushings are relatively soft, they wear out fairly quickly and a worn sprue bushing can cause sprues to stick in the stationary mold half. To improve the wear resistance of sprue bushings used in molds for thermoset materials, we suggest using sprue bushings made out of D-2 steel. These sprue bushings can be hardened to 62 HRC and they will also have higher chrome content than conventional sprue bushings. Both of these qualities should improve the wear resistance and the release properties of the sprue bushing.
Sprue Pullers
In order to insure that the sprue comes out of the sprue bushing and stays with the runner, a sprue puller is used. As can be seen in the sketch, a 5° reverse taper on the puller that starts at the runner and extend 8 mm (5/16") below the runner is recommended. In addition, a small radius (approximately 1.5 mm (1/16")) at the junction of the puller and the runner and a larger radius (approximately 6 mm (¼")) at the junction of the sprue and the runner is used to help hold the sprue, runner and sprue puller together. The added step on the bottom of the sprue puller is an aid to the removal of the sprue and sprue puller.
Sprue Bushing Locator Ring
Standard locating rings provide no support for the center of the mold. In some cases it may be necessary to have support in the middle of the stationary side of the mold. (i.e. heavy flashing in the center of the mold.) Stationary side support can be accomplished by switching to the modified locating ring shown below. This type design allows the center of the stationary side to be "domed", by placing shims under the locator ring.
Runner Design
When designing runners for molds, there are a number of possible approaches. These include the standard full round with a centerline.
This is the most efficient runner, but in some cases it is necessary for the runner to be in only one half of the mold. A standard trapezoid runner is often used in situations that require the runner to be only in one mold half. The effective runner size is shown in the figure to the left. The four corners become "dead" areas with nearly no material movement. To reduce the amount of scrap in the runner, a modified trapezoid runner design is suggested. This design reduces the dead areas without a significant change to the effectiveness of the runner.
Gates
The gates for thermoset molds are high wear areas of the mold and therefore, need to be designed with this thought in mind. The gate should be made using a replaceable insert so when the gate becomes badly worn it can be easily replaced. A gate should be made of materials that do not wear easily. Three materials commonly used for gate inserts are carbide, D-2 steel and CPM-10V particle steel made by Crucible Steel. In addition to inserting the gate, it is beneficial to insert the mold opposite the gate and at the impingement area in the cavity. These areas are also high wear locations and will need some maintenance as the mold is run. When designing an edge gate for thermoset materials, the width of the gate can be as small as 1.5 mm (1/16") but the depth of the gate should not be less than 1.3 mm (0.050"). A gate should be large enough to allow the part to fill within the range of injection pressure and injection time that Plenco suggests in the material’s “Injection Molding Startup Procedure” section. Avoid using multiple gates on parts to minimize the number of knitlines. A knitline is created when two fronts of material meet. Knitlines are weaker than the rest of the part because there is not as much cross linking that takes place across the knit as there is in the main body of the part. To keep the overall strength of the parts as high as possible, the number of knitlines should be kept to a minimum. A second type of gate that is widely used in molds processing thermoset materials is the subgate. This type of gate is sometimes referred to as a tunnel gate. The advantage of a subgate is it shears off as the part is ejected from the mold. As a result, there is no need for a secondary operation to remove the gate nor is there any concern that the gate will project out from the part and become an assembly or a visual problem. In addition to the gate removal feature, the subgate can sometimes be designed to direct the flow of material towards a difficult to fill location. In this way, the part can be made easier to fill, which can have a positive effect on cycle times and scrap rates. Gate size is dependent on the size of the part. Typically 0.13mm (0.050") can be used for small parts and 0.20mm (0.080") for larger parts. There are some problems associated with using subgates, which include:
The tip of the gate breaking off and sticking in the mold. This is especially true for polyester molding materials and therefore, the use of subgates in molds for polyester parts is not recommended. The amount of steel at the parting line above the gate being too thin which results in the metal wearing away very quickly after the mold begins to produce parts.To reduce the likelihood of the gate tip breaking off and sticking in the mold, the tunnel needs to be well polished so all EDM pits are removed. Locating an ejector pin at least 38 mm (1½") from the tunnel allows the runner to flex and pull the gate out of the mold without breaking. It is also important to design the tunnel so the angle of incidence with the part allows the gate to pull, but keeps sufficient thickness of steel at the parting line to prevent breakage. See the sketch for further clarification.
Recent developments in thermoset injection molding have shown that a part can be molded with nearly all signs of the gate gone. This is done using a gate cutter. A gate cutter is a blade or a pin that is located in the mold directly below the gate. Immediately after the material is injected into the cavity, this blade is advanced forward to seal off the gate. Once the lade is in the forward position, the material cures against it, producing the same finish as the rest of the part. The only visible trace of a gate is a witness line.
Cavities and Core
In nearly all molds, the use of inserted cavities and cores is encouraged. The primary reason for this is in the event of an individual cavity or core being damage, that particular cavity can be removed from the mold and repaired while the rest of the mold is put back into service. Having individual cavities also allows for insert changes that make it possible to run multiple versions of the same basic part simultaneously. When the parts are very small and there are a large number of cavities, individual cavity inserts might not be feasible. In those situations, we would suggest using cavity inserts of 3 or 4 cavities. The materials most commonly used for cavity inserts are H-13 and S-7. Both of these materials will harden to Rockwell 52 to 54 HRC and can be polished to produce an excellent surface finish on the parts.
Ejector Pin Location and Design
Without ejector pins, it is usually not possible to remove the molded part from the mold. The placement of the ejector pins is almost as critical as the location of the gate. The pins should push the part out of the mold without distorting it and without leaving an objectionable mark on the part. A secondary reason for having ejector pins is to aid in the venting of the mold. Ejector pins should be located in the deepest points of the cavity or core. We specifically suggest that ejector pins be located on the deepest points of ribs and bosses. If ejector pins are not located correctly, the part has to be “pulled” out of the deeper areas or the mold. Parts that have to be “pulled” out of the mold are more likely to stick or be distorted during ejection. (See sketch below.)
Once the location of the ejector pins is determined, the pin size needs to be decided upon. Very small diameter ejector pins can be problematic because of their susceptibility to breaking. Therefore, ejector pins smaller in diameter than 2.4 mm (3/32") are not recommended. Another common problem is material flowing down around the ejector pin and jamming it so it breaks when the ejectors are actuated. To prevent this from happening, the hole for the pin should only be 0.025 mm (0.001") larger than the pin for a depth of 13 mm - 16 mm (½" - _") from the cavity. Making it deeper can result in the pin binding and breaking.
To ensure that the ejector plate moves along the centerline of the ejector pins, it is suggested that the mold be equipped with a guided ejector system. In addition to aligning the ejectors, the guided ejector system moves the load of the ejector plate and the retainer plate from the ejector pins to the guide pins and bushings of the ejector system. While aligning the ejector holes in the mold with those in the retainer plate is always important, with a guided ejector system the alignment is even more critical. While it is desirable to have the ejector pins located on flat surfaces, this is not always possible. It is sometimes necessary to locate ejector pins on contoured surfaces. Ejector pins located on contoured surfaces should be made to match the contour of the cavity. It will be necessary to key these pins so they will maintain their alignment with the contour of the cavity. Sometimes parts may want to stay in the stationary mold half or a mold designer will install a stationary side ejector system as a precaution. For a compression or transfer mold this is not a problem. However, adding an ejection system to the stationary half of an injection mold can be complicated, since it will add 76.2mm – 101.6mm (3” – 4”) to the height of the mold. Therefore the amount of press daylight will need to be reviewed to make sure the mold can be opened and the parts ejected. This added length will not only increase the amount of scrap, but due to the larger sprue diameter at the parting line, the cycle time may have to be increased.
Polishing and Plating
The trend has been to cut back on polishing because of its high cost. Molds are being made that still show cutter marks on the non-visible areas of the parts. While this practice may save money in the construction of the mold, it may increase part costs due to high scrap and down time. The non-polished areas will generate frictional heat in the material as it passes over these areas. This added heat can cause the material to cure prior to filling the part. These unpolished areas can change the filling pattern of the material, which can result in gas being trapped in locations that can not be vented. For these reasons, that it is suggested that all molding surfaces be polished to a minimum of SPI #2 rating. The mold surfaces to be polished include the cavities and cores, the vents, the gates, the runners, the sprue and the entire parting line. The reason for polishing the parting line is to insure that any flash that may occur on it will come off of the mold with a minimal amount of effort.
When polishing a mold, care should be taken to be sure to always polish in the direction of draw. Vents need to be polished in the direction of material flow and they should have the same degree of polish as the cavity and core. Flat surfaces that have no influence on the removal of the part can be polished in any direction. When polishing deep ribs that were cut using the EDM process, it is important to be sure to polish out all of the EDM pit marks. Otherwise, there may be a problem with the rib breaking off of the part and sticking in the mold. After the mold is completely polished, then it is ready to be plated. Please keep in mind that any defect in the steel surface will not be covered by the plating, but will be accentuated by it. While there are a number of different types of plating available, to date, chrome plated molds provide the best part release and with the best part finish. Because some materials have fillers that are incompatible with nickel, the use of nickel or electrolysis nickel to plate molding surfaces is discouraged. In addition, nickel plating lacks the wear resistance of chrome plating. The surfaces to be plated should include the cores, the cavities, the core pins, the ends of the ejector pins, the runner blocks, the vents, and the entire parting line. To protect the molding surfaces and to insure good part release, it is necessary to plate all the surfaces that were polished. After the mold is plated, it will be necessary to repolish the chrome because unpolished chrome plating may cause sticking.
Center Supports
Often we find that molds built to run thermoset materials have little or no support in the middle. This will result is heavy flash around the sprue and parts that vary in thickness from the sprue side to the side opposite. To resolve this problem we suggest installing substantial support pillars down the center of the mold between the parallels (50.8mm (2”) dia. If possible).
High Centering the Mold
Sometimes the center of a mold will have heavy flash even with good center support. In these cases it may be necessary to do what we call “Doming the Mold” or “High Centering the Mold”. This is accomplished by placing a 0.0508mm – 0.0762mm (0.002” or 0.003”) shim on the support pillars in the center of the mold, which will cause the moving side of the mold to be slightly domed. On the stationary side of the mold we suggest using the modified locating ring shown below, that can also be shimmed 0.0508mm – 0.0762mm (0.002” or 0.003”) so this side of the mold can also be domed.
Side Locks
Injection-Compression molds require non tapered side locks and are also necessary for any molds where maintaining the alignment of the mold halves is critical to meeting the quality requirements of the part. They should be located on all four sides of the mold. The overall design of Progressive Components’ side locks is very good, since they have a longer engagement and are thicker.
Injection-Compression Mold
We suggests the following items be used in designing an Injection/Compression mold. (Also see sketch below)
• The clearance between the cavity and core should be 0.0254mm – 0.0508mm (0.001’ - 0.002”) per side.
• The engagement of the cavity into the core should be 19.050mm (0.750”).
• The shutoff around each cavity should be 0.0254mm – 0.0508mm (0.001” - 0.002”).
• The “pancake” thickness should be 0.152mm – 0.203mm (0.006” - 0.008”).
• A vent should be ground into the plunger directly opposite the sprue. This vent should start out at a depth of 0.127mm (0.005”).
• There should be a mismatch in radii between the plunger and cavity as shown, so the ejector pins have material to push against.
• The ejector pins for the “pancake” should be located around the perimeter for better and more complete flash removal.
• To prevent damaging the parting line around each cavity, landing blocks should be added that have an area equal to the maximum clamp tonnage of the press divided by 5.
Because of the close fit of the plunger and cavity, we recommend the use of non-tapered side locks to align the core and cavity.
Types of injection moulding machines
The types of injection machinery available differ basically in the method of heating and preplasticisation of the compounded rubber. The main difference usually arises between vertically oriented machines, which include both ram and screw-ram presses, and horizontally oriented machines, which are of the reciprocating screw type. In the former the mold temperature is maintained by conduction from the heated platens of the press, whereas the heaters are integral with the mold in the latter case. The configuration of molds for horizontal machines often result in large surface areas for potential convective heat loss and long paths for conductive heat flow from the press platens. The horizontal machine generates its own preplasticising heat by work on the rubber, which is fed into it in strip form, between the screw and the barrel. This heat is governed by a temperature-controlled fluid medium (water, glycol, or oil), which circulates around the barrel and, in larger machines, through the center of the screw. Progression of the rubber up the screw both heats and preplasticises it. The rubber, collected in front of the screw, pushes the screw back until a trip switch is operated, and the preplasticisation phase is completed. Final heating of the stock takes place during passage through a small die into the runner system of the mold. The second type of injection press uses the principle of vertical injection. This type of machine has a separate screw and injection piston in a V-head configuration situated near a vertical upstroking press. The preplasticising screw feeds into the injection chamber through a non-return valve where the compound is injected into the mold. There are many independently adjustable parameters of both the injection head and press unit. Molds for vertically oriented machines are usually larger in plan area, giving improved conductive heating, and also expose smaller areas for convective heat loss.
- ATTACHMENTS
-
TipsOnMoldDesign.pdf- Original PDF article by Mahesh P Deshmukh
- (571.98 KiB) Downloaded 81 times
MATI is truly a one-stop shopping source for the molding and mold making industries, offering everything from standard ejector pins to complex runner less molding systems with precision temperature controllers in India.
ReplyDeleteI would highly recommend Le_ meridian funding services to any person in need financial help and they will keep you on top of high directories for any further needs. Once again I commend yourself and your staff for extraordinary service and customer service, as this is a great asset to your company and a pleasant experience to customers such as myself. Wishing you all the best for the future.Le meridian funding service is best way to get an easy loan,here is there email..lfdsloans@lemeridianfds.com / lfdsloans@outlook.com Or talk to Mr Benjamin On WhatsApp Via_+1-989-394-3740 Thank You for helping me with loan once again in my sincerely heart I'm forever grateful.
ReplyDelete